Open Gear and Wire Rope Grease NLGI-0 Product Data Sheet
ANDEROL OGWR-0 is aluminum complex soap based grease for lubrication of open gears
and/or wire ropes. It is formulated with a high quality mineral oil fortified with fine particles of
graphite and chemically active EP additives.
ANDEROL OGWR-0 grease is designed for automatic spray lubrication of toothed wheels,
gear rings, toothed racks and pinions of any kind under high pressure and temperature
operations. It suits for lubrication of rotary furnaces or similar hot lubricating points even under
dusty and wet conditions.
APPLICATIONS / ADVANTAGES REGISTRATIONS / APPROVAL HANDLING AND STORAGE
Applicable with spray diffusers
High thermal load capacity
High pressure load capacity
Resistant to water exposure
Good corrosion protection
Very good adhesiveness
ANDEROL Lubricants are approved,
recommended and field tested by
many OEM’s
ANDEROL lubricants generally present little
hazard in normal handling if ordinary care is
exercised. If spilled, cover with inert,
absorbent material and remove. Flush the
area with water.
Although ANDEROL lubricants are not highly
flammable, they will burn and should be kept
away from open flames. In case of fire, use
water spray, foam, carbon dioxide, or dry
chemical.
ANDEROL lubricants should be stored
preferably in protected locations to prevent
contamination. Do not re-use drums; flush
and send to reconditioner.
FOR MORE INFORMATION PLEASE REFER TO THE RELEVANT MATERIAL SAFETY DATA SHEET
APPROVALS / REGISTRATIONS
This information is furnished without warranty, representation, inducement, or license of any kind except that it is accurate to the best of OUR knowledge or obtained from sources believed by
ANDEROL to be accurate. ANDEROL does not assume any legal responsibility for use of reliance upon it. Only Chemists or chemically qualified lab technicians should carry out tests. Before using any
chemicals, read its label and Material Safety Data Sheet.
PROPERTIES TEST METHOD ANDEROL OGWR-0
Thickener
Color
Type of Base Oil
Operating temperature for long-term lubrication
Short time admissible temperature peak value
Dropping Point
Worked Penetration
Base Oil Viscosity at 40° C
Water resistance
Corrosion Protection
Copper Corrosion at 120° C
4-Ball Weld Load
FZG Gear Rig Test, A/2, 8/50
- Damage force grade
- Specific weight change
Designation
DIN ISO 2176
DIN ISO 2137
DIN 51.562
DIN 51.807-01
DIN 51.802
DIN 51.811
DIN 51.350/4
DIN 51.502
Aluminum Complex
Mineral
-20 to +200° C
+250° C
>240° C
355 to 385 0.1 mm
Approx. 500 mm²/s
0-90
Corrosion degree 0
Corrosion degree 1
7000 n
> 12
< 0.27 mg/kWh
OGPF 0 S-20 |